http://dspace.bsu.edu.ru/handle/123456789/51498| Название: | The grain-refinement mechanism during heavy cold-rolling of commercial-purity titanium |
| Авторы: | Mironov, S. Zherebtsov, S. Semiatin, S. I. |
| Ключевые слова: | technique metal science commercial-purity titanium cold rolling ultrafine-grain materials electron backscatter diffraction microstructure |
| Дата публикации: | 2022 |
| Библиографическое описание: | Mironov, S. The grain-refinement mechanism during heavy cold-rolling of commercial-purity titanium / S. Mironov, S. Zherebtsov, S.I. Semiatin // Journal of alloys and compounds. - 2022. - Vol.895, P.2.-Art. 162689. - URL: https://www.sciencedirect.com/science/article/pii/S0925838821040998 |
| Краткий осмотр (реферат): | Microstructure evolution in heavily-cold-rolled (≥40 pct.) commercial-purity titanium was determined to be governed by a continuous-dynamic-recrystallization mechanism. This process was shown to be closely linked with mechanical twinning occurring at lower rolling strains |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/51498 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |