http://dspace.bsu.edu.ru/handle/123456789/4742| Название: | Laves phase evolution in a modified P911 heat resistant steel during creep at 923 K |
| Авторы: | Kipelova, A. Belyakov, A. Kaibyshev, R. |
| Ключевые слова: | metal technology steel production steels electron microscopy martensite creep precipitation coarsening grain boundary tungsten molybdenum |
| Дата публикации: | 2012 |
| Библиографическое описание: | Kipelova, A. Laves phase evolution in a modified P911 heat resistant steel during creep at 923 K / A. Kipelova, A. Belyakov, R. Kaibyshev ; Belgorod State University // Materials science and engineering A. - 2012. - Vol.532.-P. 71-77. - doi: 10.1016/j.msea.2011.10.064. |
| Краткий осмотр (реферат): | The evolution of Fe2(W, Mo) Laves phase in a 3%Co modified P911 heat resistant steel was examined during creep tests at 923 K. It is assumed that the evolution of Laves phase during creep is controlled by the grain boundary diffusion of tungsten and molybdenum |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/4742 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Kipelova_Laves phase.pdf | 887.51 kB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.