http://dspace.bsu.edu.ru/handle/123456789/59175| Название: | Strengthening mechanisms in a medium-carbon steel subjected to thermo-mechanical processing |
| Авторы: | Dudko, V. Yuzbekova, D. Kaibyshev, R. |
| Ключевые слова: | technique metal science plasticity methods iron alloys grains and interfaces electron microscopy |
| Дата публикации: | 2023 |
| Библиографическое описание: | Dudko, V. Strengthening mechanisms in a medium-carbon steel subjected to thermo-mechanical processing / V. Dudko, D. Yuzbekova, R. Kaibyshev // Applied Sciences. - 2023. - Vol.13, №17.-Art. 9614. |
| Краткий осмотр (реферат): | Strengthening mechanisms were examined in a Fe-0.43C-1.60Si-0.01Mn-1.1Cr-0.95Mo- 0.08V-0.05Nb steel exhibiting a yield strength (YS) of 1310 MPa after tempering and 1550 MPa after tempforming. The dislocation strengthening gave a major contribution to the overall YS of the steel in the tempered condition, whereas dispersion strengthening was a major contributor to the YS of the steel in the tempformed condition |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/59175 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |