http://dspace.bsu.edu.ru/handle/123456789/42712| Название: | Fabrication of bismuth films by a melt spinning method and the influence of annealing on their microstructure |
| Авторы: | Kozhemyakin, G. N. Kovalev, S. Yu. Soklakova, O. N. |
| Ключевые слова: | technique metal science bismuth melt spinning method films crystallites annealing nanocrystals |
| Дата публикации: | 2020 |
| Библиографическое описание: | Kozhemyakin, G.N. Fabrication of bismuth films by a melt spinning method and the influence of annealing on their microstructure / G.N. Kozhemyakin, Kovalev S.Yu., O.N. Soklakova // Inorganic Materials: Applied Research. - 2020. - Vol.11, №3.-P. 727-730. - Doi: 10.1134/S2075113320030259. - Refer.: p. 730. |
| Краткий осмотр (реферат): | The conditions of fabrication of bismuth films with thickness from 5 to 30 μm by a melt spinning method were studied. The microstructure of the fabricated films in the cross section was analyzed using SEM. The Bi films with thickness more than 5 μm consisted of crystallites with sizes up to 30 μm and had a layered structure with crystal twins |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/42712 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Soklakova_Fabrication.pdf | 797.81 kB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.