|Title:||Hot deformation behavior and processing maps of B and Gd containing β- solidified TiAl based alloy|
|Authors:||Sokolovsky, V. S.|
Stepanov, N. D.
Zherebtsov, S. V.
Nochovnaya, N. A.
Salishchev, G. A.
|Citation:||Hot deformation behavior and processing maps of B and Gd containing β- solidified TiAl based alloy / V.S. Sokolovsky [et al.] // Intermetallics. - 2018. - Vol.94.-P. 138-151. - Doi: https://doi.org/10.1016/j.intermet.2018.01.004.|
|Abstract:||High-temperature mechanical behavior and microstructure evolution during hot deformation of an as-cast β-solidified Ti-43.2Al-1.9V-1.1Nb-1.0Zr-0.2Gd-0.2B (at.%) alloy were studied. Phase transformation temperatures and associated phase fields (α2 + γ, α + γ, α, and α + β) were established by Thermo-Calc calculations, dilatometry, differential scanning calorimetry and microstructure analysis of specimens annealed at different temperatures. The as-cast alloy was subjected to uniaxial compression at temperatures from 900 to 1250 °C and strain rates in the range 0.001-1 s-1|
|Appears in Collections:||Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages)|
|Stepanov_Hot deformation.pdf||6.86 MB||Adobe PDF||View/Open|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.