Modelling of the rolling process of titanium alloy tube billets in laboratory conditions on a RSP 14-40 rolling mill

Abstract

The development of screw rolling technology for the production of hot-deformed tubes over Ø250 mm on a SVP-500 rolling mill faces a number of challenges that influence the quality of tubes, such as: the screw trace formed on the external surface of tubes and bending of tubes that makes impossible subsequent manufacturing operations. The following experimental and laboratory research was performed to solve these problems: a number of experimental tube billets with and without mandrels were rolled to various strains on a RSP 14-40 laboratory rolling mill to obtain the best ratio of wall thickness to the external diameter