http://dspace.bsu.edu.ru/handle/123456789/31541| Название: | Aging behavior of the HfNbTaTiZr high entropy alloy |
| Авторы: | Stepanov, N. D. Yurchenko, N. Yu. Zherebtsov, S. V. Tikhonovsky, M. A Salishchev, G. A. |
| Ключевые слова: | physics metals alloys high entropy alloys phase transformation heat treatment TEM |
| Дата публикации: | 2018 |
| Библиографическое описание: | Aging behavior of the HfNbTaTiZr high entropy alloy / N. D. Stepanov, N. Yu. Yurchenko, S. V. Zherebtsov [et al.] // Materials Letters. - 2018. - Vol.211. - P. 87-90. |
| Краткий осмотр (реферат): | The HfNbTaTiZr high entropy alloy was produced by vacuum arc melting, homogenized at 1200 C, and annealed at 600-1000 C for 1-100 h. Structure and microhardness of the annealed alloy were investigated. A strong increase of microhardness after aging treatment at 600 C was found. Formation of second hcp phase particles in the bcc matrix after annealing at 600 and 800 C was also revealed. Effect of precipitation of second phase particles on microhardness was analyzed |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/31541 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Stepanov_Aging.pdf | 1.33 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.