http://dspace.bsu.edu.ru/handle/123456789/31298| Название: | Microstructure evolution of a ti/tib metal-matrix composite during high-temperature deformation |
| Авторы: | Ozerov, M. S. Klimova, M. V. Stepanov, N. D. Zherebtsov, S. V. |
| Ключевые слова: | physics metal-matrix composite spark plasma sintering uniaxial compression dynamic recrystallization activation energy precipitation hardening |
| Дата публикации: | 2018 |
| Библиографическое описание: | Microstructure evolution of a ti/tib metal-matrix composite during high-temperature deformation / M. S. Ozerov, M. V. Klimova, N. D. Stepanov [et al.] // Materials Physics and Mechanics. - 2018. - Vol.38, N1. - P. 54-63. |
| Краткий осмотр (реферат): | A Ti/TiB metal-matrix composite (MMC) was produced by spark plasma sintering using a Ti-10wt.%TiB2 powder mixture at 850°C under a load of 40 MPa for 15 min. The microstructure evolution and mechanical behavior of the Ti/TiB composite during uniaxial compression at the temperature range 500 - 1050°С was studied |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/31298 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Ozerov_Microstructure.pdf | 1.63 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.