http://dspace.bsu.edu.ru/handle/123456789/30327| Название: | Mechanical behavior and microstructure evolution of a Ti-15Mo/TiB titanium–matrix composite during hot deformation |
| Авторы: | Zherebtsov, S. Ozerov, M. Klimova, M. Moskovskikh, D. Stepanov, N. |
| Ключевые слова: | technique metal science titanium–matrix composite microstructure evolution deformation mechanicalproperties |
| Дата публикации: | 2019 |
| Библиографическое описание: | Mechanical behavior and microstructure evolution of a Ti-15Mo/TiB titanium–matrix composite during hot deformation / S. Zherebtsov, M. Ozerov, M. Klimova [et al.] // Metals. - 2019. - Vol.9, №11.-Art. 1175. |
| Краткий осмотр (реферат): | A Ti-15Mo/TiB titanium–matrix composite (TMC) was produced by spark plasma sintering at 1400◦C under a load of 40 MPa for 15 min using a Ti-14.25(wt.)%Mo-5(wt.)%TiB2 powder mixture. Microstructure evolution and mechanical behavior of the composite were studied during uniaxial compression at room temperature and in a temperature range of 500–1000◦C. |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/30327 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |