http://dspace.bsu.edu.ru/handle/123456789/28415| Название: | Recrystallized microstructures and mechanical properties of a C-containing CoCrFeNiMn-type high-entropy alloy |
| Авторы: | Klimova, M. V. Shaysultanov, D. G. Chernichenko, R. S. Stepanov, N. D. Zherebtsov, S. V. Belyakov, A. N. |
| Ключевые слова: | technique metal science alloys high-entropy alloys mechanical properties phase transformations cold rolling electron microscopy stress/strain measurements |
| Дата публикации: | 2019 |
| Библиографическое описание: | Recrystallized microstructures and mechanical properties of a C-containing CoCrFeNiMn-type high-entropy alloy / М.V. Klimova [et al.] // Materials Science & Engineering A. - 2019. - Vol.740-741.-P. 201-210. - Refer.: p. 209-210. |
| Краткий осмотр (реферат): | The effect of cold rolling to 80% thickness reduction and annealing at 973-1373 K for 1h our on the microstructure and mechanical properties of a C-containing CoCrFeNiMn high-entropy alloy was studied. Cold rolling significantly strengthened the alloy to the yield strength of 1310 MPa. Annealing at 973 K or 1073 K resulted in incomplete recrystallization of an fcc matrix and M23C6-type carbide precipitations aligned with highly elongated grains/subgrains. Complete recrystallization occurred during annealing at 1173-1373 K |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/28415 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Klimova_Recrystallized.pdf | 3.3 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.